Journal of Analytical Methods in Chemistry

Journal of Analytical Methods in Chemistry / 2020 / Article

Research Article | Open Access

Volume 2020 |Article ID 6026312 |

Eman Alzahrani, "Colorimetric Detection Based on Localized Surface Plasmon Resonance Optical Characteristics for Sensing of Mercury Using Green-Synthesized Silver Nanoparticles", Journal of Analytical Methods in Chemistry, vol. 2020, Article ID 6026312, 14 pages, 2020.

Colorimetric Detection Based on Localized Surface Plasmon Resonance Optical Characteristics for Sensing of Mercury Using Green-Synthesized Silver Nanoparticles

Academic Editor: Miren Lopez de Alda
Received27 Jul 2019
Revised23 Sep 2019
Accepted17 Oct 2019
Published11 Jan 2020


Development of selective colorimetric detectors that can use green-fabricated silver nanoparticles’ () with localized surface plasmon resonances () to rapidly, simply, and selectively detect ions was undertaken in this study. Onion extract was used for synthesising photo-induced green crystalline silver nanoparticles (). The formation of nanoparticles is enhanced when ultrasound irradiation is present; bioligands could serve as stabilizing and reducing agents. Different methods of measurement, including UV-Vis, , and , are effective for characterization of nanoparticles. The spherical nature of green-fabricated is confirmed by TEM. High-density, spherical, and uniformly formed silver nanoparticle shapes were found in silver nanoparticle SEM images. The arrangement of in the form of face-centered cubic structures was confirmed by patterns. The formation of impurity-free was confirmed using the analysis results. with excellent sensitivity was sensitively and selectively detected by employing green-synthesized silver nanoparticles. The reduction of (1) to (0) was confirmed by a slight increase in (II) concentration and progressive reduction of green-synthesized , whose absorbance changed abruptly. The reduction of by the phosphate buffer medium enables to sensitively and selectively detect ions by providing good environment. Besides, a selective, sensitive, simple, and rapid method that is proposed for detecting (II) ions in samples of water is presented in the study. Harmful mercury ions in real samples of water (tap and ground water) can colorimetrically and selectively be detected using the. The results showed an RSD of below 6% and over 92% of good recovery.

1. Introduction

The ecological environment and human health are seriously threatened by toxicity associated with heavy-metal ion contamination [14]. Dye, coal, plastic, paper, and natural gas industries exemplify heavy metal pollution sources [57]. Because of its highly toxic compounds, mercury ions () present a significant concern among numerous heavy metals. Even in low concentrations, intestines, stomach, kidney, heart, and brain can be spoilt by , which is among the most stable inorganic form of solvated mercuric ions [810]. In view of this, close attention should be accorded to selective detection of low concentration mercuric ions in biological systems and waste water; additionally, all contaminated products should be examined to identity the quantity of . Drinking water should have concentration limits of not more than 2 ppb for mercury ions, as outlined in the Environmental Protection Agency () and World Health Organization () requirements [11, 12].

Mercury ion detection can be undertaken using classical methods. Nevertheless, tedious laboratory procedures and expensive instruments complicate the use of such methods. In view of this, there is an increasing need for developing ion sensors that could be considered convenient, straightforward, cost-effective, real time, and on-site. Numerous ion detection systems, including nanostructures [13, 14], DNA [15], proteins [16], polymers [1719], and organic compounds [20, 21], have been reported in the literature. Because of the sensitive reaction that metallic nanoparticles have towards the nanoparticle surface local environment, significant attention has recently focused on their chemical sensing applications. Moreover, monitoring is simplified because they exhibit strong absorption or scattering. Because of the unique optical and electronic properties of silver and gold nanoparticles (NPs), they have become suitable for detecting different analytes than other metallic nanoparticles [22, 23]. Development of numerous gold particle- () based colorimetric sensors for detecting ions has been undertaken. The area of silver nanoparticle- () based detection system [24, 25] has received less research attention.

Significant research attention in the development of mercury sensors has been accorded to , particularly because of soft-soft chemistry involving sulfur with stabilizing ligands on surfaces, thus changing the peak position and absorbance intensity, the presence of redox chemistry involving (°) and leading to formation of mixture through nanoparticle etching, high sensitivity of localized surface plasmon resonances, and cost-effective synthesis [2]. Besides, a spectrophotometer containing specific optical properties and which use LSPRs within the visibility range of 350–800  can be used for easy monitoring of [2631]. Radiation chemical reductions [32], photo reduction within reverse micelles [33], and chemical stabilisation with reagents, including sodium borohydride, ascorbate, and sodium citrate [3437] have been used for synthesizing silver nanoparticles. The aforementioned methods cannot be scaled upwards easily for large-scale nanoparticle fabrication and require toxic chemicals, energy, pressure, or temperature, as well as high costs [38]. Moreover, the use of silver nanoparticles could be limited by the absorption of toxic chemicals on silver nanoparticle surfaces [39]. Biological methods involve the use of fungus [40], enzymes [41], or microorganisms [42, 43]; nevertheless, such methods require special attention to be accorded for preparation of cultures and methods to isolate the fabricated silver nanoparticles [44, 45]. Fabrication of silver nanoparticle using green chemistry would present numerous benefits that include less energy consumption, easy scaling up for large-scale nanoparticle fabrication, high yields, low cost, eliminates the necessity for special preparation of cultures and method of isolation, and environmentally friendly [44, 4650].

Notably, the use of green-fabricated silver nanoparticles as the colorimeter detector in determining ions within phosphate buffer media that suppresses strong interference effects from other ions has received little research attention; in view of this, this study sought to fabricate green for sensitive and selective colorimetric sensing within phosphate buffer media that suppresses strong interference effects from other ions on the basis of LSPR with green silver nanoparticles acting as the case of the model. To prevent use of hazardous or toxic chemicals, an eco-friendly technique was used for fabricating nanoparticles. Under ultrasonic irradiation, were fabricated using extract of onion as the reducing reagent of silver nitrate salt (). Fourier transform-infrared spectroscopy (), analysis, analysis, analysis, and spectra analysis were used for characterising the materials prepared. On the basis of reduced surface plasmon resonance () through a spectrophotometer as well as change in visual colour from yellow to colourless, less than 2 minutes could be used for detecting . Samples of real drinking water were used to perform experiments that had high selectivity to ions. Besides, evaluation of the detection method in terms of calibration properties was undertaken.

2. Experimental

2.1. Chemicals and Reagents

A grocery store in Saudi’s city of Taif supplied fresh onions. All chemicals were analytically graded. Acros Organics (Loughborough, UK) supplied the analytical grades of silver nitrate () (99.8%) and various metal salts (MnCl2, HgCl2, CdCl2, ZnCl2, CuCl2, NiCl2, CoCl2, SrCl2, BaCl2, CaCl2, KCl, NaCl, FeCl3, AlCl3, and CrCl3) employed in the study; no further purification was done on all the aforementioned. The required quantity of salt was mixed in double-distilled water to prepare all metallic salt solutions that were used in the experiments. Moreover, , , sodium metaborate, boric acid, Na2HPO4, and NaH2PO4 were used for preparing 0.1 M buffer solution. No further purification was done to all the chemicals used in the experiment. Distilled water was used for preparing all solutions.

2.2. Instrumentation

Fisher Scientific Co. Ltd., from Shanghai, China, supplied the bath sonicator (42 kHz, 100 W). Cambridge Instruments from the United Kingdom supplied a scanning electron microscope (). JEOL Ltd from Welwyn Garden City, UK, supplied the transmission electron microscopy () instrument. A JEOL JSM 6390 LA analytical device from Tokyo, Japan, was used for conducting the energy dispersive X-ray () analysis. Thermo Scientific™ GENESYS 10S from Toronto, Canada, supplied the UV-Vis spectrophotometer. A Bruker diffractometer D8-ADVANCE alongside CuKα1 radiation from Coventry, UK, was used for obtaining diffraction patterns. A PerkinElmer ×2 device alongside DRIFT attachment and diamond ATR supplied by PerkinElmer from Buckinghamshire, UK, was used for collecting the attenuated total reflectance () mode.

2.3. Fabrication of the Green Nanoparticles

After top skin of the onion was peeled (∼20 ) and each segment separated, it was placed in room temperatures for 2 days. Filtration was conducted to the new solution to obtain onion extract concoction that is pale white and transparent, whereas the pieces of solid onion were removed, and prepared onion extract was utilised for synthesizing nanoparticles. The concoction of onion extract measuring 20 mL was combined with in distilled water (15 ) to create a total volume of 50  with a final concentration of . The concoctions were placed in the ultrasonic for 50 minutes, which yielded a light-orange colour, an indication that silver nanoparticles had been formed. The concoction was allowed to stay for 3 hours, yielding a deep brown-yellow colour. For removal of excessive free extracts of onion from the concoction, a 15-minute centrifugation was undertaken at 7,000 rpm for dispersions of silver nanoparticles. Finally, double-distilled water used to wash the formed Ag nanoparticles. Overall, the brownish residue is spread within double-distilled water and utilised for additional experiments.

2.4. Characterisation of the Green-Fabricated

An ultraviolet-visible spectrophotometer was used for monitoring the fabricated silver nanoparticle solution, whereas the silver nanoparticle formation and solution colour were observed using naked eyes. A spectrophotometer was used for measuring the absorbance for the 1 mL sample solution, which was compared against 1 mL distilled water as the blank in the range of 350–800  operated at 1 nm resolution.

TEM analysis was used for studying silver nanoparticle formation. Here, 5  sample solutions were placed onto lacey carbon-coated copper grids with a diameter of 3 mm. A Gatan Ultrascan 4000 digital camera connected to a JEOL 2010 transmission electron microscope running at 20  was used to obtain TEM images.

SEM was used for classifying silver nanoparticles in terms of morphologies. In the high vacuum mode, 100  of probe current alongside 20 kV increasing voltage was used for obtaining images. A 15-minute centrifugation at 1100 rpm was used for separating fabricated silver nanoparticles. The fabricated silver nanoparticles’ chemical composition was obtained using the energy dispersive -ray () analysis.

A spectrophotometer with a wavenumber ranging from 4000 to 600  and 4  resolution accuracy was used for obtaining a spectrum. A ratio of 1 : 100 was used for mixing KBr and the ground sample. Afterwards, clear thin pellets were made after pressing. Recording of the spectra was done in the mode of transmittance as the wavenumber function.

XRD alongside radiation (=1.5405 ) within the 2-theta () range of 35°–80° was used for performing structural analysis and phase identification.

2.5. General Procedure for the Colorimetric Determination of

Generally, the procedure for colorimetric determination involved triple dilution of double-distilled deionized water, which yielded a three-fold diluted concentration. The ability of metal ions to detect transition-metal ions (Cd2+, Co2+, Hg2+, Zn2+, Cu2+, Mn2+, and Ni2+), alkaline Earth (Ba2+, Sr2+, and Ca2+), representative alkali (K+ and Na+), trivalent metal ions (Fe3+, Al3+, and Cr3+), and green-synthesized silver nanoparticles of similar concentration (10−3 mol L−1 and 1 ), and conditions were investigated by adding 2 mL of three times diluted solution of freshly prepared silver nanoparticle solution and 0.1 M buffer solution measuring 100 . Room temperature was used for monitoring the absorption spectra changes and the assays. After 2 minutes of mixing, a digital camera was used for taking photographs.

Indeed, the linear correlation involving the unreacted silver nanoparticles after loading mercury ions followed by the conventional galvanic reaction and the measured intensity of absorption constitutes the premise for the quantitative feedback titration approach. For construction of the calibration curve (vs volume), the change in conventional absorbance strength at optimum absorption wavelength was measured in form of absorption ratio denoted by the following equation [51, 52]:where and denote the maximum absorbance for the absorption band of LSPR (subscripts “” and “” represent the blank colloidal suspension prior to injection of required analyte concentration, as well as at infinite duration).

2.6. Recovery Experiments

Finally, three separate concentrations of mercury ions spiked with tap and ground water samples were used for performing the recovery experiments. Afterwards, mercury ion concentration in samples was computed using the linear regression equation and the assay response against samples of spiked water. Accordingly, the formula below was used for computing the recovery values [53]:

3. Results and Discussion

3.1. Formation of Green

For use in analytical applications, stable silver nanoparticles should be synthesized against the dilution, over ionic strength, different pH ranges, and long storage period [28, 48, 52]. In this study, wet-chemical green synthesis was used for preparing the green silver nanoparticles because it constituted the most prevalent procedure for fabricating uniform nanoparticles with regulated sizes and strong silver nanoparticles alongside their colloidal dispersions in organic solvents or water [5456]. The onion extract as an eco-friendly reducing reagent and nontoxic bioextract that reduced silver ions () to colloidal silver nanoparticles (°) was used for performing the reduction under a sonication bath. In the current study, ultrasonic irradiation was employed at the expense of magnetic stirring as past study reported [51], a significant reduction of alongside a higher formation of silver nanoparticles when utilising sonication bath, an indication that the reaction rate could be enhanced through ultrasonic irradiation.

3.2. Characterisation of the Green
3.2.1. Optical Studies

Visual observation for silver nanoparticle formation is facilitated when colour change follows the conversion of silver ions to silver nanoparticles. In view of this, silver nanoparticle formation was monitored by visually checking the colour changes, and when the colour of the solution does not change further, the reaction was halted [5759]. There was a gradual change in reaction mixture’s colour from colourless into brown in 50 minutes because of silver nanoparticle formation within the solution, as illustrated in Figure 1(a). This is because of excitation of surface plasmon vibrations in AgNPs [60].

The solution and the green-fabricated silver nanoparticles in terms of the spectra are illustrated in Figure 1(b). The results showed that the solution had no absorbance, while the silver nanoparticles had an absorbance peak. A narrow, symmetrically sharp, and single LSPR band contained the colloidal solution’s absorption spectra. The silver nanoparticles had an optimum absorbance peak of 405 nm, thus implying the presence of a slight-blue change as opposed to the optimum absorbance of between 410 and 422 nm for silver nanoparticles [6163]. Thus far, the change characterising silver nanoparticle bands lacks a general principle. Nevertheless, dielectric environment, shape, and size differences could be the cause of band shift [6467]. The final conversion of solution into AgNPs reached 100% in 50 minutes since the maximum absorbance of the formed AgNPs were not increased. After one month, the fabricated silver nanoparticles remain unaffected, an indication of stability and uniform dispersal for green-fabricated silver nanoparticles within aqueous solution. Besides, the green-prepared silver nanoparticles could be preserved in form of lyophilized powder over a prolonged period without the LSPR property shifting [68].

3.2.2. Morphological Characterisation

In this study, TEM analysis that can account for fabricated nanoparticle size and morphology was used for characterising green-fabricated silver nanoparticles [28, 69, 70]. Different magnifications for green-fabricated silver nanoparticle TEM micrographs are illustrated in Figure 2. The findings showed that the silver nanoparticles were within the nanorange with spherical shape and with good dispersal and without aggregation. In addition, a thin capping material layer from onion extract on the surface of AgNPs was observed, which can help stabilize the AgNPs in the solution for long period [71].

The green silver nanoparticles suspended in sterilized distilled water were utilised for SEM analysis through fabrication of suspension drops onto clean electric stubs, and the water was left to evaporate completely. The silver nanoparticles’ SEM image indicated uniformly shaped and spherical nanoparticle formation with onion extract synthesizing high-density silver nanoparticles, a further confirmation of existing monodispersed silver nanoparticles, as illustrated in Figure 3. The same result was obtained by Jae Song and Beom Kim [60].

3.2.3. Analysis

Quantitative and qualitative data for fabricated material elements could be given through EDAX analysis. In view of this, EDAX analysis was used for green-fabricated silver nanoparticles. The sample’s elemental composition is shown by the EDAX spectrum in Figure 4. Due to surface plasmon resonance, an optical absorption peak at 3 , and peaks at between 2  and 4 , associated with silver’s properties lines L and K [60, 72, 73] was found. This showed the presence of silver in the nanostructure. In addition, other aspects could be seen on the left side of EDAX spectrum, that is, sodium () at 1.041  and oxygen () at 0.525 . The tested samples sodium and oxygen peaks appeared from the biomolecules, which are bound to silver nanoparticle surface, and created a thin capping material layer and had stability in solution because of capping materials on the nanoparticle surface. For other groups, a similar outcome was obtained [74, 75].

The quantitative analysis was conducted using the obtained EDAX spectrum. The results showed that oxygen and sodium contents were 35.93% and 23.98%, whereas silver content was high at 40.09% within the samples examined. The EDAX analysis results revealed formation of pure silver nanoparticles.

3.2.4. Analysis

X-ray diffraction was used for analyzing the crystallinity of synthesized silver nanoparticles. XRD diffraction peaks of 76°, 64°, 46°, and 38° that correspond to crystal facets for (3 1 1), (2 2 0), (2 0 0), and (1 1 1) were found, as illustrated in Figure 5. There is significant concurrence between face-centred cubic () structure [76, 77] crystal and the peaks, an indication of crystalline silver presence in silver nanoparticles. Diffraction peaks that corresponded to the precursors () or by-products (for instance, silver oxide) did not exist, thus confirming that in situ formation of metallic silver was only possible through reaction of onion extracts. The high crystallinity level for the synthesized silver nanoparticles is reflected by the peak intensity. Nevertheless, the breadth of diffraction peaks is an indication of small sizes of crystallite. This is consistent with the findings of Kumar et al. [78], Balavigneswaran et al [79], and Sheny et al. [80].

3.2.5. Measurement

The green-fabricated silver nanoparticles’ spectrum after spectroscopy was conducted, as illustrated in Figure 6. The stretching vibration, stretching vibration, and organic moiety such as carboxylic acid cause an intense broad band at 3400 cm−1. There is correspondence between polysaccharide-oriented aromatic stretching vibrational modes and anionic carboxylate group and the absorption band at 1660  [81]. This is in good agreement with the report done by Alzahrani et al. [52, 82]. The nanoparticles gain further stability when functionalization of silver nanoparticles that herbal extracts synthesized is undertaken using polysaccharides and aromatic compounds as documented within the FT-IR analysis. Silver ions within silver nanoparticles may be caused by aromatic compounds that exist within plant extracts.

3.3. Colorimetric Sensor

Metallic ion forms could accidentally be released when metals are extensively used in different fields [83]. Water bodies and the environment face pollution from such metal ions. Owing to its existence in different forms including organic, inorganic, and elemental, mercury is regarded as the most toxic of all listed pollutants [84]. Conventional systems of detecting metal ions could be considered labour intensive or expensive [85]. The silver nanoparticles’ SPR properties to detect transition metal ions, alkaline metal ions, alkali metal ions, and mercury ions were explored in this paper.

3.3.1. Detection of Alkali, Alkaline, and Trivalent Metal Ions

As Section 2.5 describes, 2 mL silver nanoparticle solution was added to 10−3 L−1 and 1  concentration containing salt stock solution to investigate how green-synthesized silver nanoparticles react to alkaline and alkali Earth metals. Afterwards, metal ion solutions were added creating an overall volume of 3 mL to investigate how different metal ions affected the LSPRs band intensity and the UV-Vis absorption spectra that corresponded were documented.

Absorption titrations were performed against alkaline metal ions such as Sr2+, K+, Ca2+, Na+, and Ba2+ ions and alkali metal to investigate the ability of green-fabricated silver nanoparticles to detect these ions. Based on the illustration in Figure 7(a), the silver nanoparticles’ absorbance ratio and mixture colour were checked after the interaction of different alkaline metal ions and alkali metals. No change in silver nanoparticle colour was observed when alkaline metal ions or alkali metals were added to silver nanoparticles. The silver nanoparticle solution’s UV-Vis absorbance after and before 1 mL of various alkaline metal ions or alkali metals was added and is illustrated in Figure 7(b). A change in spectrum was not observed for alkaline metal ions or alkali metals, and the optimum absorption wavelength of silver nanoparticles was found to be about 405 . Changes in colour and LSPR absorption were not observed.

The colorimetric reaction of silver nanoparticles to different alkaline metal ions and alkali metals is illustrated in Figure 7(c). The detector’s selectivity for these metal ions with green-fabricated silver nanoparticles was not observed. The same result was obtained when trivalent metal ions (Fe3+, Al3+, and Cr3+) was used to check the ability of the green-fabricated silver nanoparticles to detect these metal ions (Figure 8).

3.3.2. Detection of Transition Metal Ions

The study investigated how silver nanoparticle solution was affected by transition metal ions. This was undertaken by examining various heavy metals including Zn2+, Hg2+, Co2+, Cd2+, Cu2+, Ni2+, and Mn2+ ions. Unlike other metals, there was a significant colour change in silver nanoparticles for transition metal ions after mercury ions were added, as illustrated in Figure 9(a). The results showed that when mercury ions were added to glass tubes that contained freshly prepared silver nanoparticle solution, there was a colour change for silver nanoparticle solution from brown to transparent; however, for transition heavy metals, there was no change after the silver nanoparticle solution was added, which implies the absence of effect on silver nanoparticle colour. In addition, it was found that the assay method has high specificity and selectivity toward mercury ions and alkaline metal, alkali metal, and other transition metal ions in similar conditions do not experience silver nanoparticle sensitivity.

The silver nanoparticles’ UV-Vis absorbance after and before addition of 1 mL of various transition metal ions is illustrated in Figure 9(b). Unlike mercury ions that caused a change in spectrum, the silver nanoparticle colour and LSPR band did not experience any effect; in addition, the maximum wavelength had decreased absorbance, and there was apparition for new LSPR bands at longer UV-Vis spectra wavelength. The optical spectroscopic signatures for closed-shell configuration Hg2+ do not exist [66]. After mercury was added to silver nanoparticles, solution colour changed to colourless and the silver nanoparticles did not have the LSPR band.

To further study the selective nature of silver nanoparticles towards different metal ions, the silver nanoparticle solution’s absorbance was plotted with all transition metal ions. The selective nature of the optimized mercury ion sensor was examined by comparing solutions of other metallic ions against the silver nanoparticle absorbance ratio . The silver nanoparticles intensity ratios of different metal ions clearly showed selectivity for mercury II ions, as illustrated in Figure 9(c). All the observations and results obtained indicate that aggregates of silver nanoparticles whose colour was transparent accounted for a significant ratio, whereas good dispersal of silver nanoparticles was demonstrated by a lower ratio [86]. By comparing Figures 7(c) and 8(c) with Figure 9(c), it is obvious that the absorption ratio ( of the green-fabricated silver nanoparticles with different metals (alkali, alkaline, trivalent, and transition metal ions) was less than 1.0 a.u. except for mercury, which was more than 2.5 a.u. These findings showed that silver nanoparticles had a reactive selectivity towards mercury II ions, as the dramatic absorbance ratio increased.

3.3.3. Investigation of Different Volumes of Mercury Ions

To examine the sensitive nature of the method and the minimum detectable mercury II ion within aqueous solutions by monitoring the values of UV-Vis absorbance and the system’s colour change, different volumes of mercury ions’ aqueous solution were incorporated to 2 mL silver nanoparticle solution in room temperatures. UV-Vis spectra for the silver nanoparticle LSPR property was used to determine the mercury II ion detection limit. There was a change in colour from yellow, light yellow, and light salmon to clear/transparent after different volumes of mercury II solution was introduced incrementally from 0 to 1400 , as illustrated in the photograph for silver nanoparticle solution in Figure 10(a). Notably, the trend is significantly attributed to silver nanoparticle oxidation by mercury II ions caused by greater mercury/mercury ion potential (0.851 ), as opposed to silver/silver ions (0.799 ) [52, 87]. The reduction of silver nanoparticle LSPR band intensity was visible with mercury II ions. Because of this, a redox reaction will occur between mercury and silver ions. An amalgam of mercury and silver is formed when mercury II ions are reduced to mercury by the electrochemical reduction potential difference from oxidized silver nanoparticles [85].

Because of the colour change for silver nanoparticle solution, a UV-Vis spectrometer could be used for monitoring the change in LSPR optical properties. Figure 10(b) illustrates the correlation between mercury II ion and changes in the absorbance strength of LSPR. It could be inferred that the strength of LSPR absorbance changed significantly, and this was dependent on mercury II ion volume. Based on the figure, it could be stated that when mercury II ion increased, the absorbance peak of silver nanoparticles decreased. In addition, the absorption band of the surface plasmon might experience a slight change of blue shift when mercury II ions are increased. Findings have shown that reduction of mercury ions within aqueous silver solution from mercury layers around particles of silver could be undertaken radiolytically, followed by plasmon absorption band’s blue shift and broadening [88]. Based on conducted experiments, metallic mercury was formed after silver nanoparticles reacted with the mercury II ion. The silver surface could offer the platform for strong bonding of newly generated mercury atoms, and this might be accounted for by slight-blue changes of the silver nanoparticles’ LSPR band. The results could be considered the initial stage in the investigation of mercury ion detection. Indeed, a digestive technique can be used for transforming different forms of mercury such as , , , , and [89]. In view of this, the proposed study might provide a significant promise as the method for colorimetrically detecting overall forms of mercury.

Figure 10(c) illustrates the plot for colorimetric response () against the mercury II ion volume through a construction of the absorption spectra that produced the calibration curve ( vs volume). A linear correlation (), between the mercury II ion volume and absorbance intensity, changes in the range of 0  to 1400  at 405 . In view of this, it could be inferred that mercury II ion could be detected colorimetrically using green-synthesized silver nanoparticles. Sakly et al. [53] fabricated AgNPs coated with carboxymethyl cellulose (CMC-capped AgNPs) from date palm tree for Hg2+ ion detection with 95% of good recovery, and RSD does not exceed 8%. Although the recovery in this study is slightly low (92%) compared with the previous study, the detection method was fast, simple, and selective colorimetric assay for ions. In addition, the procedure for fabrication of green AgNPs using onion extract was simple and fast.

After addition of mercury II ions, TEM analysis was used for examining the fabricated silver nanoparticles. Contrary to the results in Figures 2 and 11 showed that the introduction of mercury II ions completely changed the silver nanoparticles’ morphology. The absorbance of the LSPR band had effective excitation, which was attributed to the dispersion media having dispersed and stable silver nanoparticles prior to addition of mercury II ions. In contrast, the introduction of mercury II ions to silver nanoparticles caused aggregation of nanoparticles through catalytic reactions between ions and silver nanoparticles; notably, the nanoparticle aggregation decreased the absorbance strength of the LSPR band. In addition, silver nanoparticle aggregation did not exist alongside other metal ions.

3.4. Practical Application

Notably, real samples of water were used at the micromolar level for evaluating the feasibility of the proposed detection method for mercury II ions. A specific volume obtained from the sample with drinking water was added to as-prepared colloidal solution that was spiked initially using aqueous solution (overall concentration 250 ) before each sample was loaded with toxic ion. There was no detection of LSPR absorption spectra, regardless of the composition. Different mercury II ions mixed with spiked samples of drinking water were used for performing recovery experiments. Based on the results in Table 1, a relative standard deviation (RSD) of below 6% and suitable recovery of over 92% were obtained. In addition, the table indicates that mercury II ion detection was not interfered with the composition of water samples. Besides, measurement repeatability was conducted on 3 colloidal solution replicates under similar experimental conditions. Because the RSD does surpass 6%, the proposed assay could be considered reliable as confirmed by the results. Moreover, consistent with results, mercury poisoning could be prevented by potentially applying the proposed colorimetric assay.

SampleSpiked (μM)Recovery (%)RSD (%) n = 3

Ground water30097.85.97
60098. 64.82

Tap water30095.25.88

RSD = relative standard deviation.

4. Conclusion

Overall, a selective, highly sensitive, rapid, ecofriendly, cost-effective, label-free, and simple colorimetric assay to detect mercury II ions in samples of drinking water using green-prepared silver nanoparticles and onion extracts as the colorimetric probe, which allow mercury II ions to be detected in real time and rapidly, has been developed. Good stability and localized surface plasmons are exhibited by the green-synthesized silver nanoparticles. A similar chemistry is used for silver nanoparticle lowering LSPRs to etch out silver ions during mercury II ion sensing. Selective, rapid, cost-effective, and simple mercury II ion sensing within real water and biological samples in the future will benefit from this chemistry. Accordingly, plasmonic-assisted colorimetric assays for detecting mercury II ion will be enhanced when methodologies are enriched, and new approaches were applied through successful and full implementation of the eco-friendly colorimetric assay. Currently, the focus is on developing highly sensitive and selective (up to picomolar or nanomolar concentration range) for detection of hazardous metal ions using silver nanoparticles stabilized using onion extracts.

Data Availability

The data used to support the findings of this study are included within the article.

Conflicts of Interest

The author declares that there are no conflicts of interest.


  1. S. Mishra, R. N. Bharagava, N. More et al., “Heavy metal contamination: an alarming threat to environment and human health,” in Environmental Biotechnology: For Sustainable Future, pp. 103–125, Springer, Singapore, 2019. View at: Publisher Site | Google Scholar
  2. J. Zhang, X. Sun, and J. Wu, “Heavy metal ion detection platforms based on a glutathione probe: a mini review,” Applied Sciences, vol. 9, no. 3, pp. 489–507, 2019. View at: Publisher Site | Google Scholar
  3. P. Saha and B. Paul, “Assessment of heavy metal toxicity related with human health risk in the surface water of an industrialized area by a novel technique,” Human and Ecological Risk Assessment: an International Journal, vol. 25, no. 4, pp. 966–987, 2018. View at: Publisher Site | Google Scholar
  4. H. Eijsackers, A. Reinecke, S. Reinecke, and M. Maboeta, “Heavy metal threats to plants and soil life in southern Africa: present knowledge and consequences for ecological risk assessment,” Reviews of Environmental Contamination and Toxicology, vol. 249, pp. 29–70, 2019. View at: Publisher Site | Google Scholar
  5. P. C. Nagajyoti, K. D. Lee, and T. V. M. Sreekanth, “Heavy metals, occurrence and toxicity for plants: a review,” Environmental Chemistry Letters, vol. 8, no. 3, pp. 199–216, 2010. View at: Publisher Site | Google Scholar
  6. U. Förstner and G. T. Wittmann, Metal Pollution in the Aquatic Environment, Springer Science & Business Media, Berlin, Germany, 2012.
  7. J. W. Moore and S. Ramamoorthy, Heavy Metals in Natural Waters: Applied Monitoring and Impact Assessment, Springer Science & Business Media, Berlin, Germany, 2012.
  8. S. Ghosh, S. Maji, and A. Mondal, “Study of selective sensing of Hg2+ ions by green synthesized silver nanoparticles suppressing the effect of Fe3+ ions,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 555, pp. 324–331, 2018. View at: Publisher Site | Google Scholar
  9. T. W. Clarkson, L. Magos, and G. J. Myers, “The toxicology of mercury—current exposures and clinical manifestations,” New England Journal of Medicine, vol. 349, no. 18, pp. 1731–1737, 2003. View at: Publisher Site | Google Scholar
  10. Y. Wang, F. Yang, and X. Yang, “Colorimetric biosensing of mercury(II) ion using unmodified gold nanoparticle probes and thrombin-binding aptamer,” Biosensors and Bioelectronics, vol. 25, no. 8, pp. 1994–1998, 2010. View at: Publisher Site | Google Scholar
  11. M. Update, “Impact on fish advisories,” Tech. Rep., Office of Water, Washington, DC, USA, 2001, EPA fact sheet EPA-823-F-01-011. View at: Google Scholar
  12. F. Edition, “Guidelines for drinking-water quality,” WHO Chronicle, vol. 38, no. 4, pp. 104–108, 2011. View at: Google Scholar
  13. M. Rex, F. E. Hernandez, and A. D. Campiglia, “Pushing the limits of mercury sensors with gold nanorods,” Analytical Chemistry, vol. 78, no. 2, pp. 445–451, 2006. View at: Publisher Site | Google Scholar
  14. C.-C. Huang and H.-T. Chang, “Selective gold-nanoparticle-based “turn-on” fluorescent sensors for detection of mercury(II) in aqueous solution,” Analytical Chemistry, vol. 78, no. 24, pp. 8332–8338, 2006. View at: Publisher Site | Google Scholar
  15. J. Liu and Y. Lu, “Rational design of “turn-on” Allosteric DNAzyme catalytic beacons for aqueous mercury ions with ultrahigh sensitivity and selectivity,” Angewandte Chemie International Edition, vol. 46, no. 40, pp. 7587–7590, 2007. View at: Publisher Site | Google Scholar
  16. S. V. Wegner, A. Okesli, P. Chen, and C. He, “Design of an emission ratiometric biosensor from MerR family proteins: a sensitive and selective sensor for Hg2+,” Journal of the American Chemical Society, vol. 129, no. 12, pp. 3474-3475, 2007. View at: Publisher Site | Google Scholar
  17. Y. Zhao and Z. Zhong, “Tuning the sensitivity of a foldamer-based mercury sensor by its folding energy,” Journal of the American Chemical Society, vol. 128, no. 31, pp. 9988-9989, 2006. View at: Publisher Site | Google Scholar
  18. X. Liu, Y. Tang, L. Wang et al., “Optical detection of mercury(II) in aqueous solutions by using conjugated polymers and label-free oligonucleotides,” Advanced Materials, vol. 19, no. 11, pp. 1471–1474, 2007. View at: Publisher Site | Google Scholar
  19. I.-B. Kim and U. H. F. Bunz, “Modulating the sensory response of a conjugated polymer by proteins: an agglutination assay for mercury ions in water,” Journal of the American Chemical Society, vol. 128, no. 9, pp. 2818-2819, 2006. View at: Publisher Site | Google Scholar
  20. S. Yoon, A. E. Albers, A. P. Wong, and C. J. Chang, “Screening mercury levels in fish with a selective fluorescent chemosensor,” Journal of the American Chemical Society, vol. 127, no. 46, pp. 16030-16031, 2005. View at: Publisher Site | Google Scholar
  21. C.-K. Chiang, C.-C. Huang, C.-W. Liu, and H.-T. Chang, “Oligonucleotide-based fluorescence probe for sensitive and selective detection of mercury(II) in aqueous solution,” Analytical Chemistry, vol. 80, no. 10, pp. 3716–3721, 2008. View at: Publisher Site | Google Scholar
  22. G. A. Messina, M. Regiart, S. V. Pereira et al., “Nanomaterials in the development of biosensor and application in the determination of pollutants in water,” in Advanced Research in Nanosciences for Water Technology, pp. 195–215, Springer, Berlin, Germany, 2019. View at: Publisher Site | Google Scholar
  23. L. Tamayo, H. Palza, J. Bejarano, and P. A. Zapata, “Polymer composites with metal nanoparticles: synthesis, properties, and applications,” Polymer Composites with Functionalized Nanoparticles, Elsevier, Amsterdam, Netherlands, 2019. View at: Google Scholar
  24. C. Sönnichsen, B. M. Reinhard, J. Liphardt, and A. P. Alivisatos, “A molecular ruler based on plasmon coupling of single gold and silver nanoparticles,” Nature Biotechnology, vol. 23, no. 6, pp. 741–745, 2005. View at: Publisher Site | Google Scholar
  25. Y. Wang, F. Yang, and X. Yang, “Colorimetric detection of mercury(II) ion using unmodified silver nanoparticles and mercury-specific oligonucleotides,” ACS Applied Materials & Interfaces, vol. 2, no. 2, pp. 339–342, 2010. View at: Publisher Site | Google Scholar
  26. M. Willander, O. Nur, Y. E. Lozovik et al., “Solid and soft nanostructured materials: fundamentals and applications,” Microelectronics Journal, vol. 36, no. 11, pp. 940–949, 2005. View at: Publisher Site | Google Scholar
  27. Y. Kobayashi, H. Katakami, E. Mine, D. Nagao, M. Konno, and L. M. Liz-Marzán, “Silica coating of silver nanoparticles using a modified Stöber method,” Journal of Colloid and Interface Science, vol. 283, no. 2, pp. 392–396, 2005. View at: Publisher Site | Google Scholar
  28. E. Alzahrani, “Eco-friendly production of silver nanoparticles from peel of tangerine for degradation of dye,” World Journal of Nano Science and Engineering, vol. 5, no. 1, pp. 10–16, 2015. View at: Publisher Site | Google Scholar
  29. D. Mandal, S. Mishra, and R. K. Singh, “Green synthesized nanoparticles as potential nanosensors,” in Environmental, Chemical and Medical Sensors, pp. 137–164, Springer, Berlin, Germany, 2018. View at: Google Scholar
  30. L. Chen, Y. Wang, X. Fu, and L. Chen, Novel Optical Nanoprobes for Chemical and Biological Analysis, Springer, Berlin, Germany, 2014.
  31. Y. Li, F. Zheng, Z. Li, and J. Laven, “Silver nanoparticles prepared by using poly(2-acrylamido-2-methylpropane sulphonic acid) as a surfactant,” Micro & Nano Letters, vol. 9, no. 10, pp. 750–752, 2014. View at: Publisher Site | Google Scholar
  32. A. Henglein, “Physicochemical properties of small metal particles in solution: “microelectrode” reactions, chemisorption, composite metal particles, and the atom-to-metal transition,” The Journal of Physical Chemistry, vol. 97, no. 21, pp. 5457–5471, 1993. View at: Publisher Site | Google Scholar
  33. Y.-P. Sun, P. Atorngitjawat, and M. J. Meziani, “Preparation of silver nanoparticles via rapid expansion of water in carbon dioxide microemulsion into reductant solution,” Langmuir, vol. 17, no. 19, pp. 5707–5710, 2001. View at: Publisher Site | Google Scholar
  34. I. Pastoriza-Santos and L. M. Liz-Marzán, “formation and stabilization of silver nanoparticles through reduction by N,N-dimethylformamide,” Langmuir, vol. 15, no. 4, pp. 948–951, 1999. View at: Publisher Site | Google Scholar
  35. S. Iravani, H. Korbekandi, S. Mirmohammadi, and B. Zolfaghari, “Synthesis of silver nanoparticles: chemical, physical and biological methods,” Research in Pharmaceutical Sciences, vol. 9, no. 6, pp. 385–406, 2014. View at: Google Scholar
  36. T. Ahmad, I. A. Wani, and S. Khatoon, “Controlling the size and morphology of silver nanoparticles: role of chemical routes,” Nanotech, vol. 1, pp. 292–298, 2011. View at: Google Scholar
  37. X. He, A. Lu, J. Cheng et al., “Overview of the application of flow microreactors in the synthesis of silver nanomaterials,” Nano, vol. 12, no. 11, p. 1730002, 2017. View at: Publisher Site | Google Scholar
  38. S. Ponarulselvam, C. Panneerselvam, K. Murugan, N. Aarthi, K. Kalimuthu, and S. Thangamani, “Synthesis of silver nanoparticles using leaves of Catharanthus roseus Linn. G. Don and their antiplasmodial activities,” Asian Pacific Journal of Tropical Biomedicine, vol. 2, no. 7, pp. 574–580, 2012. View at: Publisher Site | Google Scholar
  39. P. Liu, B.-C. Yang, G. Liu et al., “Improving power conversion efficiency of perovskite solar cells by cooperative LSPR of gold-silver dual nanoparticles,” Chinese Physics B, vol. 26, no. 5, Article ID 058401, 2017. View at: Publisher Site | Google Scholar
  40. X. Zhang, X. He, K. Wang, and X. Yang, “Different active biomolecules involved in biosynthesis of gold nanoparticles by three fungus species,” Journal of Biomedical Nanotechnology, vol. 7, no. 2, pp. 245–254, 2011. View at: Publisher Site | Google Scholar
  41. I. Willner, R. Baron, and B. Willner, “Growing metal nanoparticles by enzymes,” Advanced Materials, vol. 18, no. 9, pp. 1109–1120, 2006. View at: Publisher Site | Google Scholar
  42. S. Prabhu and E. K. Poulose, “Silver nanoparticles: mechanism of antimicrobial action, synthesis, medical applications, and toxicity effects,” International Nano Letters, vol. 2, no. 1, pp. 1–10, 2012. View at: Publisher Site | Google Scholar
  43. Y. Konishi, K. Ohno, N. Saitoh et al., “Bioreductive deposition of platinum nanoparticles on the bacterium Shewanella algae,” Journal of Biotechnology, vol. 128, no. 3, pp. 648–653, 2007. View at: Publisher Site | Google Scholar
  44. A. Saxena, R. Tripathi, and R. Singh, “Biological synthesis of silver nanoparticles by using onion (Allium cepa) extract and their antibacterial activity,” Digest Journal of Nanomaterials and Biostructures, vol. 5, no. 2, pp. 427–432, 2010. View at: Google Scholar
  45. D. Jain, H. K. Daima, S. Kachhwaha, and S. Kothari, “Synthesis of plant-mediated silver nanoparticles using papaya fruit extract and evaluation of their anti microbial activities,” Digest Journal of Nanomaterials and Biostructures, vol. 4, no. 3, pp. 557–563, 2009. View at: Google Scholar
  46. S. K. Srikar, D. D. Giri, D. B. Pal, P. K. Mishra, and S. N. Upadhyay, “Green synthesis of silver nanoparticles: a review,” Green and Sustainable Chemistry, vol. 6, no. 1, pp. 34–56, 2016. View at: Publisher Site | Google Scholar
  47. S. Ahmed, M. Ahmad, B. L. Swami, and S. Ikram, “A review on plants extract mediated synthesis of silver nanoparticles for antimicrobial applications: a green expertise,” Journal of Advanced Research, vol. 7, no. 1, pp. 17–28, 2016. View at: Publisher Site | Google Scholar
  48. E. Alzahrani and K. Welham, “Optimization preparation of the biosynthesis of silver nanoparticles using watermelon and study of itsantibacterial activity,” International Journal of Basic and Applied Sciences, vol. 3, no. 4, pp. 392–400, 2014. View at: Publisher Site | Google Scholar
  49. N. Geetha, K. Harini, J. J. Showmya, and K. S. Priya, “Biofabrication of silver nanoparticles using leaf extract of Chromolaena odorata (L.) king and robinson,” International Conference on Nuclear Energy, Environmental and Biological Sciences, vol. 8, pp. 56–59, 2012. View at: Google Scholar
  50. L. Ma, W. Su, J.-X. Liu et al., “Optimization for extracellular biosynthesis of silver nanoparticles by Penicillium aculeatum Su1 and their antimicrobial activity and cytotoxic effect compared with silver ions,” Materials Science and Engineering: C, vol. 77, pp. 963–971, 2017. View at: Publisher Site | Google Scholar
  51. P. Vasileva, B. Donkova, I. Karadjova, and C. Dushkin, “Synthesis of starch-stabilized silver nanoparticles and their application as a surface plasmon resonance-based sensor of hydrogen peroxide,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 382, no. 1–3, pp. 203–210, 2011. View at: Publisher Site | Google Scholar
  52. E. Alzahrani, “Colorimetric detection based on localised surface plasmon resonance optical characteristics for the detection of hydrogen peroxide using acacia gum–stabilised silver nanoparticles,” Analytical Chemistry Insights, vol. 12, pp. 1–10, 2017. View at: Publisher Site | Google Scholar
  53. N. Sakly, W. Marzouk, H. B. Ouada, and H. Majdoub, “Enhancing performances of colorimetric response of carboxymethylcellulose-stabilized silver nanoparticles: a fully eco-friendly assay for Hg2+ detection,” Sensors and Actuators B: Chemical, vol. 253, pp. 918–927, 2017. View at: Publisher Site | Google Scholar
  54. B. Swain, C. Mishra, H. S. Hong, and S.-S. Cho, “Selective recovery of pure copper nanopowder from indium-tin-oxide etching wastewater by various wet chemical reduction process: understanding their chemistry and comparisons of sustainable valorization processes,” Environmental Research, vol. 147, pp. 249–258, 2016. View at: Publisher Site | Google Scholar
  55. K. Rajan, I. Roppolo, A. Chiappone, S. Bocchini, D. Perrone, and A. Chiolerio, “Silver nanoparticle ink technology: state of the art,” Nanotechnology, Science and Applications, vol. 9, pp. 1–13, 2016. View at: Publisher Site | Google Scholar
  56. T. Altantzis, Z. Yang, S. Bals, G. Van Tendeloo, and M.-P. Pileni, “Thermal stability of CoAu13 binary nanoparticle superlattices under the electron beam,” Chemistry of Materials, vol. 28, no. 3, pp. 716–719, 2016. View at: Publisher Site | Google Scholar
  57. S. I. I. Abdel-Hafez, N. A. Nafady, I. R. Abdel-Rahim, A. M. Shaltout, and M. A. Mohamed, “Biogenesis and optimisation of silver nanoparticles by the endophytic fungus cladosporium sphaerospermum,” International Journal of Nanomaterials and Chemistry, vol. 2, no. 1, pp. 11–19, 2016. View at: Publisher Site | Google Scholar
  58. P. Mosae Selvakumar, C. A. Antonyraj, R. Babu, A. Dakhsinamurthy, N. Manikandan, and A. Palanivel, “Green synthesis and antimicrobial activity of monodispersed silver nanoparticles synthesized using lemon extract,” Synthesis and Reactivity in Inorganic, Metal-Organic, and Nano-Metal Chemistry, vol. 46, no. 2, pp. 291–294, 2016. View at: Publisher Site | Google Scholar
  59. A. N. D. Krupa, M. E. A. Abigail, C. Santhosh, A. N. Grace, and R. Vimala, “Optimization of process parameters for the microbial synthesis of silver nanoparticles using 3-level Box-Behnken Design,” Ecological Engineering, vol. 87, pp. 168–174, 2016. View at: Publisher Site | Google Scholar
  60. H. Bar, D. K. Bhui, G. P. Sahoo, P. Sarkar, S. P. De, and A. Misra, “Green synthesis of silver nanoparticles using latex of Jatropha curcas,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 339, no. 1–3, pp. 134–139, 2009. View at: Publisher Site | Google Scholar
  61. C. Y. Tai, Y.-H. Wang, and H.-S. Liu, “A green process for preparing silver nanoparticles using spinning disk reactor,” AIChE Journal, vol. 54, no. 2, pp. 445–452, 2008. View at: Publisher Site | Google Scholar
  62. S. Chairam and E. Somsook, “Starch vermicelli template for synthesis of magnetic iron oxide nanoclusters,” Journal of Magnetism and Magnetic Materials, vol. 320, no. 15, pp. 2039–2043, 2008. View at: Publisher Site | Google Scholar
  63. S. Chairam, C. Poolperm, and E. Somsook, “Starch vermicelli template-assisted synthesis of size/shape-controlled nanoparticles,” Carbohydrate Polymers, vol. 75, no. 4, pp. 694–704, 2009. View at: Publisher Site | Google Scholar
  64. J. P. Wilcoxon and B. L. Abrams, “Synthesis, structure and properties of metal nanoclusters,” Chemical Society Reviews, vol. 35, no. 11, pp. 1162–1194, 2006. View at: Publisher Site | Google Scholar
  65. K. L. Kelly, E. Coronado, L. L. Zhao, and G. C. Schatz, “The optical properties of metal nanoparticles: the influence of size, shape, and dielectric environment,” The Journal of Physical Chemistry B, vol. 107, no. 3, pp. 668–677, 2003. View at: Publisher Site | Google Scholar
  66. K. Farhadi, M. Forough, R. Molaei, S. Hajizadeh, and A. Rafipour, “Highly selective Hg2+ colorimetric sensor using green synthesized and unmodified silver nanoparticles,” Sensors and Actuators B: Chemical, vol. 161, no. 1, pp. 880–885, 2012. View at: Publisher Site | Google Scholar
  67. L. Guoliang, J. Lei, C. Liyuan, and P. Bing, “Preparation of nanosilver by using water-insoluble reducing agent o-phenylenediamine,” Micro & Nano Letters, vol. 7, no. 9, pp. 923–926, 2012. View at: Publisher Site | Google Scholar
  68. M. Sengan, D. Veeramuthu, and A. Veerappan, “Photosynthesis of silver nanoparticles using Durio zibethinus aqueous extract and its application in catalytic reduction of nitroaromatics, degradation of hazardous dyes and selective colorimetric sensing of mercury ions,” Materials Research Bulletin, vol. 100, pp. 386–393, 2018. View at: Publisher Site | Google Scholar
  69. G. A. Martínez-Castañón, N. Niño-Martínez, F. Martínez-Gutierrez, J. R. Martínez-Mendoza, and F. Ruiz, “Synthesis and antibacterial activity of silver nanoparticles with different sizes,” Journal of Nanoparticle Research, vol. 10, no. 8, pp. 1343–1348, 2008. View at: Publisher Site | Google Scholar
  70. Z. Yi, X. Xu, X. Wu et al., “Silver nanoplates: controlled preparation, self-assembly, and applications in surface-enhanced Raman scattering,” Applied Physics A, vol. 110, no. 2, pp. 335–342, 2013. View at: Publisher Site | Google Scholar
  71. S. S. Shankar, A. Rai, A. Ahmad, and M. Sastry, “Rapid synthesis of Au, Ag, and bimetallic Au core-Ag shell nanoparticles using neem (Azadirachta indica) leaf broth,” Journal of Colloid and Interface Science, vol. 275, no. 2, pp. 496–502, 2004. View at: Publisher Site | Google Scholar
  72. K. Murugan, C. Raman, C. Panneerselvam et al., “Nano-insecticides for the control of human and crop pests,” in Short Views on Insect Genomics and Proteomics, pp. 229–251, Springer, Cham, Switzerland, 2016. View at: Publisher Site | Google Scholar
  73. M. Govindarajan, M. Rajeswary, K. Veerakumar, U. Muthukumaran, S. L. Hoti, and G. Benelli, “Green synthesis and characterization of silver nanoparticles fabricated using Anisomeles indica: mosquitocidal potential against malaria, dengue and Japanese encephalitis vectors,” Experimental Parasitology, vol. 161, pp. 40–47, 2016. View at: Publisher Site | Google Scholar
  74. M. Puchalski, P. Dąbrowski, W. Olejniczak, P. Krukowski, P. Kowalczyk, and K. Polański, “The study of silver nanoparticles by scanning electron microscopy, energy dispersive X-ray analysis and scanning tunnelling microscopy,” Materials Science-Poland, vol. 25, no. 2, pp. 473–478, 2007. View at: Google Scholar
  75. J. Y. Song and B. S. Kim, “Rapid biological synthesis of silver nanoparticles using plant leaf extracts,” Bioprocess and Biosystems Engineering, vol. 32, no. 1, pp. 79–84, 2009. View at: Publisher Site | Google Scholar
  76. S. Joseph and B. Mathew, “Microwave-assisted green synthesis of silver nanoparticles and the study on catalytic activity in the degradation of dyes,” Journal of Molecular Liquids, vol. 204, pp. 184–191, 2015. View at: Publisher Site | Google Scholar
  77. J. Cheon and W. Park, “Green synthesis of silver nanoparticles stabilized with mussel-inspired protein and colorimetric sensing of lead (II) and copper (II) ions,” International Journal of Molecular Sciences, vol. 17, no. 12, 2006. View at: Publisher Site | Google Scholar
  78. R. Kumar, S. M. Roopan, A. Prabhakarn, V. G. Khanna, and S. Chakroborty, “Agricultural waste Annona squamosa peel extract: biosynthesis of silver nanoparticles,” Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy, vol. 90, pp. 173–176, 2012. View at: Publisher Site | Google Scholar
  79. C. K. Balavigneswaran, T. Sujin Jeba Kumar, R. Moses Packiaraj, and S. Prakash, “Rapid detection of Cr(VI) by AgNPs probe produced by Anacardium occidentale fresh leaf extracts,” Applied Nanoscience, vol. 4, no. 3, pp. 367–378, 2014. View at: Publisher Site | Google Scholar
  80. D. S. Sheny, J. Mathew, and D. Philip, “Phytosynthesis of Au, Ag and Au-Ag bimetallic nanoparticles using aqueous extract and dried leaf of Anacardium occidentale,” Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy, vol. 79, no. 1, pp. 254–262, 2011. View at: Publisher Site | Google Scholar
  81. C. Picart, A. Schneider, O. Etienne et al., “Controlled degradability of polysaccharide multilayer films in vitro and in vivo,” Advanced Functional Materials, vol. 15, no. 11, pp. 1771–1780, 2005. View at: Publisher Site | Google Scholar
  82. Y. N. Rao, D. Banerjee, A. Datta, S. K. Das, R. Guin, and A. Saha, “Gamma irradiation route to synthesis of highly re-dispersible natural polymer capped silver nanoparticles,” Radiation Physics and Chemistry, vol. 79, no. 12, pp. 1240–1246, 2010. View at: Publisher Site | Google Scholar
  83. W. Hou and S. B. Cronin, “A review of surface plasmon resonance-enhanced photocatalysis,” Advanced Functional Materials, vol. 23, no. 13, pp. 1612–1619, 2013. View at: Publisher Site | Google Scholar
  84. J. Pletz, F. Sánchez-Bayo, and H. A. Tennekes, “Dose-response analysis indicating time-dependent neurotoxicity caused by organic and inorganic mercury-Implications for toxic effects in the developing brain,” Toxicology, vol. 347–349, pp. 1–5, 2016. View at: Publisher Site | Google Scholar
  85. G. V. Ramesh and T. P. Radhakrishnan, “A universal sensor for mercury (Hg, HgI, HgII) based on silver nanoparticle-embedded polymer thin film,” ACS Applied Materials & Interfaces, vol. 3, no. 4, pp. 988–994, 2011. View at: Publisher Site | Google Scholar
  86. Y. Guo, Z. Wang, W. Qu, H. Shao, and X. Jiang, “Colorimetric detection of mercury, lead and copper ions simultaneously using protein-functionalized gold nanoparticles,” Biosensors and Bioelectronics, vol. 26, no. 10, pp. 4064–4069, 2011. View at: Publisher Site | Google Scholar
  87. A. Bard, Standard Potentials in Aqueous Solution, Routledge, Abingdon, UK, 2017.
  88. L. Katsikas, M. Gutiérrez, and A. Henglein, “Bimetallic colloids: silver and mercury,” The Journal of Physical Chemistry, vol. 100, no. 27, pp. 11203–11206, 1996. View at: Publisher Site | Google Scholar
  89. A. Fan, Y. Ling, C. Lau, and J. Lu, “Direct colorimetric visualization of mercury (Hg2+) based on the formation of gold nanoparticles,” Talanta, vol. 82, no. 2, pp. 687–692, 2010. View at: Publisher Site | Google Scholar

Copyright © 2020 Eman Alzahrani. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

More related articles

No related content is available yet for this article.
 PDF Download Citation Citation
 Download other formatsMore
 Order printed copiesOrder

Related articles

No related content is available yet for this article.

Article of the Year Award: Outstanding research contributions of 2020, as selected by our Chief Editors. Read the winning articles.